Low alloyed tool steel plate AISI S1

Model Number: ZXL115 Brand Name: Baosteel, TISCO Key Specifications/Special Features: Description:This steel is one of the high duty shock resisting tool steel types.Applications: All kinds of cold and hot pneumatic tools, cold and hot cutting shears for plate, pressing dies.Chemical Composition (in weight %) C: 0.50Si: 0.85Mn: 0.30Cr: 1.05V: 0.15W: 1.45Physical properties (averagevalues) at ambient temperatureModulus of elasticity [103xN/mm2]: 210Density [g/cm3]: 7.90Thermal conductivity [W/m. K]: 25.0Electric resistivity [Ohm mm2/m]: 0.30Specific heat capacity [J/g. K]: 0.46Soft annealingHeat to 720-750℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650℃, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening: Harden froma temperature of 890-930℃, followed by oil or water quenching. Hardness after quenching is 56-59, 61-64 HRC.
Tempering: Tempering temperature: 150-400℃ForgingHot forming temperature: Heat slowly and uniformly to 1000℃. Forge within a range of 1000/800℃ reheating if necessary. Cool slowly (preferably in a furnace) to avoid setting up stresses.
Corrosion resistance: Corrosion resistance of this alloy is better than that of plain carbon steels. However it will rust unless given protective treatment.
Specifications: Grade: mat. No. 1.2542
Standard: DIN, GB, EN, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customer's requirements.
Delivery lead time: 7-20 days after received deposit of T/T.